Quantcast WELDING PROCEDURE SPECIFICATION - WPS NO: 106

 

Click here to make tpub.com your Home Page

Page Title: WELDING PROCEDURE SPECIFICATION - WPS NO: 106
Back | Up | Next

Click here for thousands of PDF manuals

Google


Web
www.tpub.com

Home


   
Information Categories
.... Administration
Advancement
Aerographer
Automotive
Aviation
Construction
Diving
Draftsman
Engineering
Electronics
Food and Cooking
Logistics
Math
Medical
Music
Nuclear Fundamentals
Photography
Religion
   
   

 

Share on Google+Share on FacebookShare on LinkedInShare on TwitterShare on DiggShare on Stumble Upon
Back
WELDING PROCEDURE SPECIFICATION - WPS NO: 105
Up
TM-5-5420-279-23 Dry Support Bridge (DSB) (NSN
Next
WELDING PROCEDURE SPECIFICATION - WPS NO: 107
TM 5-5420-279-23
WPS No. 0106
WILLIAMS FAIREY ENGINEERING LTD.
APPROVAL REPORT:
WELDING PROCEDURE SPECIFICATION - WPS NO: 106
W.P.A.R. No: 001
Approved by:
Sheet No: 1
Issue: 1
Date: 08-08-02
K.L. No: 9526
Primary Specifications:
Material Specification:
Material Dimensions.
BS EN 729
BS 1470 Grade 5251
Thickness: 3 to 6mm
and 5251 to 232B
Pipe Dia: N/A
Aluminium
Type Of Joint:
Welding Process:
Welding Position:
Butt and fillet weld
Manual T.I.G.
ALL
Run Sequence & Weld Dimensions:
Joint Preparation:
Preparation Method: Weld areas to be degreased and wire brushed before assembly
Welding Details:
Wire feed
Travel
Heat
Size of filler
Type of
Run No.
Process
Current A
Voltage
Speed
Speed
Input
metal
Current
M/Min
mm/Min
J/mm
1
T.I.G.
1.6 - 2.4mm
80 - 220
15 - 22
A/C
N/A
N/A
Additional
T.I.G.
1.6 - 2.4mm
70 - 220
15 - 22
A/C
N/A
N/A
runs
Filler Metal Classification & BS 2901 PT 4 TYPE 5556A
Gas Type Shielding: Argon
Gas flow Shielding:
Tungsten Electrode Type:
Backing: N/A
10 - 18 cu/ft/hr
Zirconiated
Backing: N/A
Size: 2.4 - 4mm
Details of Back Cutting / Backing:
Preheat Temperature:
Interpass temperature:
Transfer Mode: N/A
Min +5C
100c
Other Information:
Dress or remove all unsound tack welds
Appendix K Page 81